Porosity; Dielectric properties; Mechanical properties; Si3N4
资金
- National Natural Science Foundation of China [91016021, 11102003]
- China Postdoctoral Science Foundation Funded Project [20110490196]
- National Basic Research Program of China [G2010CB832701]
Highly porous Si3N4 ceramics have been fabricated via freeze casting and sintering. The as-sintered samples were pre-oxidized at 1200-1400 degrees C for 15 min. The effect of pre-oxidation temperature on the microstructure, flexural strength, and dielectric properties of porous Si3N4 ceramics were investigated. As the pre-oxidation temperature increased from 1200 degrees C to 1400 degrees C, firstly, the flexural strength of the pre-oxidized specimens remained almost constant at 1200 degrees C, and then decreased to 14.2 MPa at 1300 degrees C, but finally increased to 25.6 MPa at 1400 degrees C, while the dielectric constant decreased gradually over the frequencies ranging from 8.2 GHz to 12.4 GHz. This simple process allows porous Si3N4 ceramics to have ultra-low dielectric constant and moderate strength, which will be feasible in broadband radome applications at high temperatures. (c) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据