CERAMICS INTERNATIONAL
卷 38, 期 8, 页码 6723-6728出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2012.05.063
关键词
Sintering; Dielectric properties; Ceramics; Microstructure
Ba4Nd9.33Ti18O54 x wt%Al2O3 (BNT-A) ceramics (x=0, 0.5, 1.0, 1.5, 2.0, 2.5) were prepared by the conventional solid state reaction. The effects of Al2O3 on the microstructure and microwave dielectric properties of Ba4Nd9.33Ti18O54 (BNT) ceramics were investigated. X-ray diffraction and backscatter electronic images showed that the Al2O3 additive gave rise to a second phase BaAl2Ti5O14 (BAT). The formation mechanism and grain growth of the BAT phase were first discussed. Dielectric property test revealed that the Al2O3 additive had improved the dielectric properties of the BNT ceramics: increased the Q x f value from 8270 to 12,180 GHz and decreased the tau(f) value from 53.4 to 11.2 ppm/degrees C. A BNT-A ceramic with excellent dielectric properties: epsilon(r) = 70.2, Q x f = 12,180 GHz, tau(f) =20 ppm/degrees C was obtained with 2.0 wt% Al2O3 added after sintering at 1320 degrees C for 4 h. (C) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据