Powders: chemical preparation; Sol-gel process; Perovskites; LaFeO3
资金
- Natural Science Foundation of China [10975055, 60771021]
LaFeO3 were synthesized via a sol gel route based on polyvinyl alcohol (PVA). Differential scanning calorimetry (DSC), Thermogravimetric (TG), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), Raman spectroscopy and field emission scanning electron microscopy (FESEM) techniques were used to characterize precursors and derived oxide powders. The effect of the ratios of positively charged valences to hydroxyl groups of PVA (Mn+/-OH) on the formation of LaFeO3 was investigated. XRD analysis showed that single-phase and well-crystallized LaFeO3 was obtained from the Mn+/-OH = 4:1 molar ratio precursor at 700 degrees C. For the precursor with Mn+/-OH = 2:1, nanocrystalline LaFeO3 with average particle size of 50 nm was formed directly in the charring procedure. With increase of PVA content to Mn+/-OH = 1:1, phase pure LaFeO3 was obtained at 500 degrees C. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据