DOI: 10.1016/j.ceramint.2010.10.002
关键词
LiTaO3/Al2O3 composite ceramics; Crack propagation; Domain switching; Toughening mechanism; Transmission electron microscopy (TEM)
资金
- National Natural Science Foundation of China [50602041]
- New Star Technology Plan of Beijing [2007A080]
Direct observation of crack propagation in LiTaO3/Al2O3 composite ceramics was carried out using in situ transmission electron microscopy (TEM). Domain switching induced by crack propagation, crack deflection and branching at domain boundaries and ripples similar to the contrasts of 180 degrees domains at the microcrack tip inside LiTaO3 grains were detected evidently. Domain switching, crack deflection, branching and energy dissipation resulting from the formation of contrasts similar to the 180 degrees domains at the microcrack tip, were proposed as the toughening mechanisms in LiTaO3/Al2O3 ceramics. (C) 2010 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据