关键词
Preceramic polymer; Curing; Pyrolysis; Boron nitride fiber
资金
- National 863 Program [2006AA03A217]
Boron nitride (BN) fiber with a composition of BN(1.09) was fabricated by curing and thermolysis of a novel poly[(alkylamino)borazine]. The processes have been studied by a combination of gel-content test, TGA, elemental analysis, IR, XPS, XRD, SEM and TEM. The results show that curing made polymer fiber infusible and resulted in a significant improvement of ceramic yield from 53.2 wt% to 73.8 wt% at 1000 degrees C. Moreover, pyrolysis in NH(3) at 1200 degrees C generated a nearly stoichiometric BN without carbonaceous impurities while in Ar led to a BNC material with carbon content of 6.13 wt%. The obtained amorphous BN fiber with a diameter of 13 pun displayed a tensile strength of approximately 600 MPa. Furthermore, the BN fiber illustrated good oxidation resistance in air. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据