thermal properties; glasses; rare-earth oxide; glass structure; Vickers hardness
Bi2O3 center dot 2B(2)O(3) glasses doped with La2O3 and Er2O3 were prepared by the melting-quenching method with AR-grade oxides. IR analysis was used to investigate the glass network structure. The characteristic temperatures including the glass transition temperature (T-g), crystallization temperature (T-p), and melting temperature (T-m) were estimated by DSC. The coefficient of thermal expansion (alpha), mass density (D), and Vickers hardness (H-v) were also measured. The results show that the basic network structure of Bi2O3 center dot 2B(2)O(3) glasses doped with rare-earth oxides consists of chains composed of [BO3], [BO4], and [BiO6] Units. La2O3 and Er2O3 act as network modifiers. As the doping concentrations of the rare-earth oxides were increased, T-g increased and alpha decreased, indicating that a more rigid glass was obtained. Er2O3 reduces the melting temperature and prevents glass crystallization. La2O3 contributes to the improvement of the microhardness of Bi2O3 center dot 2B(2)O(3) glass. (C) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据