Metastable and transient states of chemical ordering in Fe-V nanocrystalline alloys

Chemical ordering of the disordered alloys Fe0.78V0.22, Fe0.53V0.47, Fe0.39V0.61, and Fe0.37V0.63 was performed by annealing at temperatures from 723 to 973 K. The initial state of chemical disorder was produced by high-energy ball milling, and the evolution of order was measured by neutron diffractometry and by Fe-57 Mossbauer spectrometry. The hyperfine magnetic field distributions obtained from the Mossbauer spectra provided quantitative measurements of the number of antisite Fe atoms in the partially ordered alloys. The long-range order parameters in steady state after long annealing times were used as states of metastable equilibrium for a generally successful comparison with the metastable Fe-V phase diagram calculated by Sanchez et al. [Phys. Rev. B 54, 8958 (1996)]. For the metastable equilibrium state of order in Fe0.53V0.47 at low temperatures, the order parameters were smaller than expected. This corresponded to an abundance of antisite atoms, which were not removed effectively by annealing at the lower temperatures.