Carbonation; Calcium-silicate-hydrate (C-S-H); Microstructure; Portland cement; Calcium hydroxide
The purpose of this article is to investigate the carbonation mechanism of CH and C-S-H within type-I cement-based materials in terms of kinetics, microstructure changes and water released from hydrates during carbonation. Carbonation tests were performed under accelerated conditions (10% CO2, 25 degrees C and 65 +/- 5% RH). Carbonation profiles were assessed by destructive and non-destructive methods such as phenolphthalein spray test, thermogravimetric analysis, and mercury intrusion porosimetry (destructive), as well as gamma-ray attenuation (non-destructive). Carbonation penetration was carried out at different ages from 1 to 16 weeks of CO2 exposure on cement pastes of 0.45 and 0.6 w/c, as well as on mortar specimens (w/c = 0.50 and s/c = 2). Combining experimental results allowed us to improve the understanding of C-S-H and CH carbonation mechanism. The variation of molar volume of C-S-H during carbonation was identified and a quantification of the amount of water released during CH and C-S-H carbonation was performed. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据