CEMENT AND CONCRETE RESEARCH
卷 54, 期 -, 页码 43-54出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.cemconres.2013.08.003
关键词
Nano alumina; Temperature; Mechanical properties; Microstructure; Mortar
资金
- Housing Research Center (HRC), University Putra Malaysia
In this study, the effect of elevated temperatures on chemical composition, microstructure and mechanical properties of high strength mortars with nano alumina was investigated. Mortars with 1,2 and 3% nano alumina as cement replacement were prepared and then exposed to 100 degrees C, 200 degrees C, 300 degrees C, 400 degrees C, 600 degrees C, 800 degrees C and 1000 degrees C. XRD, DSC and SEM tests were carried out to identify chemical composition and microstructure changes in the cement matrix after being exposed to elevated temperatures. Residual compressive strength, relative elastic modulus and gas permeability coefficient of samples were also obtained. A brittleness index was defined to monitor changes in brittleness of samples after being exposed to elevated temperatures. Nano alumina enhanced compressive strength of samples up to 16% and improved residual compressive strength. An increase in the relative elastic modulus, higher energy absorption and lower permeability were also observed when 1% nano alumina was added. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据