CEMENT AND CONCRETE RESEARCH
卷 38, 期 3, 页码 312-319出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.cemconres.2007.09.027
关键词
electrical resistivity; fresh concrete; porosity; degree of hydration
This paper reports the investigations on the early hydration process of fresh concrete using a non-contact electrical resistivity measurement. The bulk resistivity development (rho(t)-t curves) and the pore solution resistivity development (rho(0)(t)-t curves) of fresh concrete, with and without fly ash replacement, were obtained for the period from casting to the age of 48 h. The porosity development (phi(t)-t curves) was obtained from the rho(t)-t and rho(0)(t)-t evolution curves with the calculated initial porosity and the measured porosity at I day by mercury intrusion porosimetry (MIP). The degree of hydration (alpha(t)-t) of the cement-based materials was then obtained based on the porosity change with time, which was caused by the increase of hydration products with a lower density as compared to that of the original cement in the hydration system. The comparison of the degree of hydration predicted from the porosities (phi(t)-t) and obtained from the experimental measurement of non-evaporable water showed a good agreement of the two. The setting and hardening behavior of fresh concrete was characterized by the characteristic points on the rho(t)-t and d rho(t)/dt-t curves. The retarded hydration caused by the fly ash incorporation could be identified by the characteristic points. (C) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据