期刊
JOURNAL OF MATERIALS RESEARCH
卷 17, 期 3, 页码 701-704出版社
MATERIALS RESEARCH SOCIETY
DOI: 10.1557/JMR.2002.0100
关键词
-
Formation of bulk Fe-based glassy alloys with high corrosion resistance was succeeded in the Fe(75-x-y)Cr(x)MoyC(15)B(10) alloy system. A large temperature interval of supercooled liquid region (DeltaT(x) of 40-90 K was obtained over a wide composition range for the Fe75-x-yCrxMoyC15B10 alloys. The Fe75-x-yCrxMoyC15B10 alloys were prepared in a bulk glassy form with diameters of 1.0-2.5 mm by copper mold casting. The bulk glassy Fe75-x-yCrxMoyC15B10 alloys exhibited high corrosion resistance in I N HCl solution. The glassy alloys containing Cr were spontaneously passivated with a wide passive region before the transpassive dissolution of Cr. The passive current density decreased significantly with an increase of alloying Cr content, indicating that the addition of Cr was effective on enhancing the corrosion resistance. Excess addition of Mo for replacing Fe in the present alloys was detrimental for the corrosion resistance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据