CELLULOSE
卷 21, 期 3, 页码 1561-1571出版社
SPRINGER
DOI: 10.1007/s10570-014-0192-8
关键词
Nanofibrillated cellulose; Carboxymethylation; Gel; Rheology; Viscosity; Homogenization
资金
- Billerud-Korsnas
- Borregaard
- De la Rue
- Hansol
- Holmen
- Kemira
- Korsnas
- Metsa Group
- Stora Enso
- Sodra
- UPM
- Evergreen Packaging
The rheological properties of carboxymethylated nanofibrillated cellulose (NFC), investigated with controlled shear rate- and oscillatory measurements, are reported for the first time. It was shown that the rheological properties of the studied system are similar to those reported for other NFC systems. The carboxymethylated NFC systems showed among other things high elasticity and a shear thinning behaviour when subjected to increasing shear rates. Further, the shear viscosity and storage modulus of the system displayed power-law relations with respect to the dry content of the NFC suspension. The exponential values, 2 and 2.4 respectively, were found to be in good agreement with both theoretical predictions and published experimental work. Furthermore, it was found that the pulp consistency at which NFC is produced affects the properties of the system. The rheological studies imply that there exists a critical pulp concentration below which the efficiency of the delamination process diminishes; the same adverse effect is also observed when the critical concentration is significantly exceeded due to a lower energy input during delamination.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据