Xylan enriched viscose fibers

In this study, a new xylan enriched viscose fiber was developed. A high molecular weight xylan with a degree of polymerization of 150-200 was added during a late stage of the viscose production process. The xylan deriving from a cold caustic extraction (CCE) of an eucalypt paper pulp was introduced to the process after xanthation and thus neither objected to any degradation conditions during alkalization nor to the xanthation step. About 90 % of the added xylan was transferred to the final fiber. A xylan content of up to 7.5 % was achieved. Fiber properties like strength showed a comparable level to the reference fibers while the water retention value was clearly raised due to the higher content of hemicelluloses. The hemicellulose distribution over the fiber cross section was investigated by enzymatic peeling. Even though a segregation of the different polysaccharides was observed, the goal of a good blending of CCE-xylan into cellulosic fibers with new interesting features was achieved.