CELLULOSE
卷 21, 期 1, 页码 301-309出版社
SPRINGER
DOI: 10.1007/s10570-013-0146-6
关键词
Nanofiber; Cellulose; Cotton fiber; Acid hydrolysis; Mercerizing
资金
- National Natural Science Foundation of China
- Civil Aviation Administration of China [61079010]
- Fundamental Research Funds for the Central Universities [3122013P001]
Cellulose nanofibers with a diameter of 70 nm and lengths of approximately 400 nm were fabricated from partly mercerized cotton fibers by acid hydrolysis. Morphological evolution of the hydrolyzed cotton fibers was investigated by powder X-ray diffraction, Fourier transform infrared analysis and field emission scanning electron microscopy. The XRD results show that the cellulose I was partially transformed into cellulose II by treatment with 15 % NaOH at 150A degrees for 3 h. The crystallinity of this partially mercerized sample was lower than the samples that were converted completely to cellulose II by higher concentrations of NaOH. The intensities of all of the diffraction peaks were noticeably increased with increased hydrolysis time. Fourier transform infrared results revealed that the chemical composition of the remaining nanofibers of cellulose I and II had no observable change after acidic hydrolysis, and there was no difference between the hydrolysis rates for cellulose I or II. The formation of cellulose nanofibers involves three stages: net-like microfibril formation, then short microfibrils and finally nanofibers.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据