期刊
CELLULOSE
卷 19, 期 2, 页码 561-574出版社
SPRINGER
DOI: 10.1007/s10570-011-9641-9
关键词
Cellulose nanofiber; Nanofiber length; Sedimentation; Nanofiber sheets
资金
- IDP Education Australia Ltd.
- Monash University
Four different cellulose nanofibers samples were prepared from northern bleached softwood kraft fibers. Fiber diameter distributions were measured from SEM images. Fiber aspect ratios ranging from 84 to 146 were estimated from fiber suspension sedimentation measurements. Three samples had heterogeneous distributions of fiber diameters, while one sample was more homogeneous. Sheet forming experiments using filters with pores ranging from 150 to 5 mu m showed that the samples with a heterogeneous distribution of fiber dimensions could be easily formed into sheets at 0.2% initial solids concentration with all filter openings. On the other hand, sheets could only be formed from the homogenous sample by using 0.5% or more initial solids content and a lower applied vacuum and smaller filter openings. The forming data and estimated aspect ratios show reasonable agreement with the predictions of the crowding number and percolation theories for the connectivity and rigidity thresholds for fiber suspensions.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据