MATERIALS CHEMISTRY AND PHYSICS
卷 74, 期 2, 页码 201-209出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/S0254-0584(01)00467-9
关键词
tantalum oxynitride films; refractive index; binding energy; reflectance; transmittance; roughness; deposition rate
Tantalum oxynitride films, Ta(N,O), were prepared by reactive RF magnetron sputtering. Investigation was made on optical properties of films deposited at various sputtering parameters such as RF power, substrate temperature and sputtering gas ratios: N,10, flow ratio and Ar fraction (Ar/(Ar + N-2 + O-2)). The deposition rates vary from 1.9 to 5.8 nm min(-1) and 5.5 to 11.8 nm min(-1), respectively, as the Ar fraction increases from 0.5 to 0.91 and N-2/O-2 flow ratio from 0.25 to 4, respectively. The deposition rates are proportional to the substrate temperature and the RF power from 1.2 to 5.5 nm min(-1), too. By using the SEM and SPM analyses. the Ta(N,O) film not only shows a columnar structure but also has a smooth surface with a RMS roughness 0.22 nm for a film as-deposited at 300 degreesC. The roughness increases to 7.0 nm after annealing at 800 degreesC for I It. The microstructure of Ta(N,O) films closely relates to the introduced N-2/O-2 flow ratios, and shows significant effects on optical properties. By TEM microstructure analysis, a fine structure, in which nano-particles embedded in an amorphous matrix, was shown. The refractive index (n) decreases from 2.29 to 1.95 in the visible wavelength region when the N-2/O-2 flow ratio changes from 4 to 1. Furthermore, the refractive index is inversely proportional to the substrate temperature and proportional to the RF power. The reflectance (0.01-0.25) and the transmittance (0.73-0.9) change with sputtering parameters. (C) 2002 Elsevier Science B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据