期刊
COMPOSITES SCIENCE AND TECHNOLOGY
卷 62, 期 16, 页码 2169-2177出版社
ELSEVIER SCI LTD
DOI: 10.1016/S0266-3538(02)00147-1
关键词
fiber/matrix; interfacial strength; aramid fiber; acoustic emission; pull-out test
Single fiber pull-out tests were carried out to investigate the influence of water absorption on the interfacial properties of aramid/epoxy composite. The fiber/matrix interfacial strength was severely decreased between 4 and 7 week immersion time in deionized water at 80 degreesC, and thereafter showed a plateau. This change with immersion time did not correspond with that of the water gain of the pull-out specimens, because the water gain did not reflect the one in the fiber/matrix interface. As a result of the degradation of the fiber/matrix interfacial strength, the pulled-out fiber surfaces of 7, 10 and 13 week wet specimen were smooth. In situ observations of interfacial crack propagation by a video microscope and an analysis of acoustic emission (AE) signals showed that AE signals obtained during the pull-out process were classified into four types according to fracture modes. AE signals detected at final unstable crack propagation and fiber breakage had high amplitude and long duration. (C) 2002 Elsevier Science Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据