4.5 Article

Sorption of tannic acid on zirconium pillared clay

期刊

出版社

JOHN WILEY & SONS LTD
DOI: 10.1002/jctb.530

关键词

tannin sorption; pillared clay; adsorption isotherms; kinetic and thermodynamic parameters; regeneration

向作者/读者索取更多资源

Zirconium pillared clay (PILC) was prepared using montmorillonite as the base clay. Adsorption of tannic acid (tannin) was studied by a batch equilibrium technique, as a function of adsorbate concentration, temperature, pH, agitation speed, particle size of the adsorbent and ionic strength. The process of uptake is governed by diffusion controlled first-order reversible rate kinetics. The higher uptake for the pH range 4.0-6.0 was attributed to external hydrogen bonding between phenolic-OH groups of tannin molecules and the hydrogen bonding sites on the clay. The removal of tannin by adsorption was found to be >99.0% depending on the initial concentration in the pH range of 4.0-6.0. The process involves both film and pore diffusion to different extents. The effects of solute concentration, temperature, agitation speed and particle size on the diffusion rate were investigated. Tannin uptake was found to increase with ionic strength due to the compression of diffuse double layers. The applicability of Langmuir and Freundlich isotherm models has been tested. The maximum adsorption capacity of PILC was found to be 45.8 mumol g(-1) of clay and the affinity constant is 2.9 x 10(-2) dm(3) mumol(-1) at 30degreesC. Thermodynamic parameters such as DeltaGdegrees,DeltaHdegrees and DeltaSdegrees were calculated to predict the nature of adsorption. The isosteric enthalpies of adsorption were also determined and found to decrease with increasing surface coverage. Regeneration with hot water (60degreesC) has been investigated for several cycles with a view to recovering the adsorbed tannin and also restoring the sorbent to its original state. Copyright (C) 2001 Society of Chemical Industry.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据