期刊
JOURNAL OF COATINGS TECHNOLOGY
卷 75, 期 936, 页码 55-64出版社
FEDERATION SOC COATINGS TECHNOLOGY
DOI: 10.1007/BF02697923
关键词
-
Preparation and characterization of weather resistant silicone/acrylic resin coatings were conducted. In order to prepare these coatings, a silicone/acrylic resin (KLD) was first prepared by an addition polymerization reaction of monomers, including n-butyl acrylate, methyl methacrylate, n-butyl methacrylate, and 3-methacryloxypropyltrimethoxysilane (MPTS). In the preparation of the silicone/acrylic resin, T-g of the acrylic copolymer was fixed at 40degreesC and the contents of MPTS were varied to be 10, 20, and 30 wt%. The weather resistant silicone/acrylic resin coatings were then prepared-by blending the synthesized silicone/acrylic resin and TiO2. The viscosity of the synthesized resin decreased with the content of MPTS, whereas the thermal stability at high temperature increased. The prepared coatings exhibited excellent adhesion to various substrates, and various physical properties of the coatings were satisfactory. The weatherability of the coatings was tested three ways: outdoor exposure test, Weather-Ometer (WOM), and QUV accelerated weatherability tester (QUV). The gloss retention, yellowness index difference, color difference, and lightness index difference were improved at high MPTS concentration. The coatings containing 30 wt% MPTS have especially good weather properties.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据