Bismuth telluride compounds with high thermoelectric figures of merit

期刊

JOURNAL OF APPLIED PHYSICS
卷 93, 期 1, 页码 368-374

出版社

AMER INST PHYSICS
DOI: 10.1063/1.1525400

关键词

-

向作者/读者索取更多资源

The thermoelectric properties of the p-type (Bi0.25Sb0.75)(2)Te-3 doped with 8 wt. % excess Te and the n-type Bi-2 (Te0.94Se0.06)(3) doped substantially with 0.07 wt. % I, 0.02 wt. % Te, and 0.03 wt. % CuBr which were grown by the Bridgman method at a rate of 6 cm/h were measured before and after annealing, where annealing was done in the temperature range from 473 up to 673 K for 2-5 h in a vacuum and a hydrogen stream. No annealing effect on the power factor was observed for the p-type specimen, but the as-grown p-type specimen exhibited a large power factor of 5.53 x 10(-3) W/mK(2) at 308 K and a low thermal conductivity of 1.21 W/mK. When the n-type specimen was annealed at 473 K for 2 h in ahydrogen stream, however, the power factor at 308 K increased significantly from 3.26 x 10(-3) to 4.73 x 10(-3) K-1 but its thermal conductivity then increased by about 3% from 1.26 to 1.30 W/mK. As a result, the maximum thermoelectric figure of merits Z at 308 K for the as-grown p- and annealed n-type specimens reached surprisingly great values of 4.57 x 10(-3) K-1 and 3.67 x 10(-3) K-1, respectively, with corresponding ZT values of 1.41 and 1.13. The present materials are sure to belong to the highest class in the Z and ZT values as bismuth telluride bulk compounds. (C) 2003 American Institute of Physics.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据