Cu2ZnSnS4 thin films were deposited on corning 7059 glass substrates without substrates heating by rf magnetron sputtering. The Cu/(Zn + Sn) ratio of the thin film sputtered at 75 W was close to the stoichiometry of Cu2ZnSnS4. However, the S/(Cu + Zn + Sn) ratio was less than the stoichiometry. The as-deposited films were amorphous and annealed in the atmosphere of Ar + S-2 (g). The annealed (1 1 2), (2 0 0), (2 2 0), (3 12) planes were conformed to all the reflection of a kesterite structure. A preferred (1 1 2) orientation was observed with the increase of the annealing temperature. The optical absorption coefficient of the thin film was about 1.0 x 10(4) cm(-1). The optical band energy was derived to be 1.51 eV. The optical absorption coefficient of the sputtered Cu2ZnSnS4 thin films was less than that of CuInS2 thin film, however, the band gap energy was more appropriate for photovoltaic materials. (C) 2002 Elsevier Science B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据