JOURNAL OF COMPOSITE MATERIALS
卷 38, 期 6, 页码 495-514出版社
SAGE PUBLICATIONS LTD
DOI: 10.1177/0021998304040559
关键词
damage tolerance; fractography; CFRP; sandwich; CAI
In the present study, non-crimp fabric (NCF) composite face sheet sandwich panels have been tested in compression after impact (CAI). Damage in the face sheets was characterised by fractography. Compression after impact loaded panels were found to fail by plastic fibre microbuckling (kinking) in the damaged face sheet. Studies of panels for which loading was interrupted prior to failure revealed extensive stable kink band formation at several positions and in numerous plies. Kink bands initiated and propagated within a wide region close to the point of impact. In addition, kink bands initiated in zones with high shear stresses, away from the impact centre line. Consequently, the fractographic results from this investigation do not support the assumption of modelling the impact damage as an equivalent hole. To achieve accurate predictions of kink band initiation, the stress field must be known. The results from this study imply that bending effects caused by remaining dent or material eccentricities in the damaged region must be considered.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据