期刊
JOURNAL OF MATERIALS CHEMISTRY
卷 14, 期 10, 页码 1640-1647出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/b314157h
关键词
-
Nanosize crystalline cathode materials of LiNiyMn2-yO4 (0 < y <= 0.5) composition and spinel-type structure have been obtained by a single-step sucrose-aided self-combustion method. The as-prepared samples contained some amorphous organic impurities that were removed after a short period of heating at 500 degrees C. The pure single-phase spinels have been characterized by X-ray diffraction, transmission electron microscopy, chemical analysis, and nitrogen sorption isotherms. The samples consist of particles (ca. 24 nm size) that are aggregated in clusters (ca. 1 mm size) in which mesopores (10-80 nm size) appear among the particles. Additional heating at 800 degrees and 1000 degrees C produces a slight increase in the cubic lattice parameter and a pronounced increase in particle size (>100 nm). Electrical conductivity decreases as the Ni content increases in accordance with an electron hopping mechanism between Mn3+ and Mn4+ ions. The 500degreesC- and 800degreesC-heated LiNi0.5Mn1.5O4 samples show good electrochemical behaviour at 4.7 V as cathode materials. The capacity (132.7 mA h g(-1)) found is close to the nominal capacity (146.7 mA h g 21) and remains constant for current densities in the range C/24-2C (where C = 2.6 mA cm(-2)). At higher current densities (2C-10C) the capacity decreases progressively. The cyclability at the C current density is ca. 99.7% for both samples.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据