期刊
INTEGRATED FERROELECTRICS
卷 62, 期 -, 页码 177-182出版社
TAYLOR & FRANCIS LTD
DOI: 10.1080/10584580490457163
关键词
SrBi2Ta2O9; aqueous solution-gel; thin film; heat treatment
Sr0.9Bi2.2Ta2O9 thin films were prepared on a Pt-substrate by aqueous chemical solution deposition. The applied heat treatment seems to have a significant influence on the ferroelectric response, crystallinity and surface morphology. For two-layer thin films annealed at 700degreesC in oxygen, the P-r-value increased from 3.6 until 5.5 muC/cm(2), c-axis preferred orientation was considerably lowered and rod-like instead of spherical grains were grown when the second pyrolysis step at 520degreesC was omitted.