Monolithic carbon/nano-silicon composites with a three-dimensionally ordered macroporous (3DOM) structure were synthesized via a nanocasting route using a macro- and mesoporous silica monolith as a hard template for carbon with similar hierarchical porosity, followed by chemical vapor deposition to infiltrate mesopores with silicon nanoparticles. Diiodosilane was used as the silicon precursor to produce nano-silicon upon thermal decomposition. X-ray photoelectron spectroscopy revealed the presence of both elemental silicon and oxidized silicon in the porous carbon. Silicon was dispersed uniformly inside 3DOM carbon without forming large agglomerates. The as-synthesized material was Xray amorphous. A lithiation experiment showed an initial charge capacity of 920 mAh g(-1) and a reversible Li+ capacity of 332 mAh g(-1) for the carbon/nano-silicon composite. The lower-than-expected capacity is attributed to partial oxidation of nanosized silicon in the composite structure. A mechanism for decomposition of diiodosilane in this system is proposed. (C) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据