关键词
TEMPO; Cellulose nanofibril; Nanofibril length; Film properties; Oxygen permeability
资金
- Grants-in-Aid for Scientific Research [23688020, 21228007, 24880013] Funding Source: KAKEN
Various mechanical disintegration conditions in water were applied to 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO)-oxidized cellulose to prepare TEMPO-oxidized cellulose nanofibrils (TOCNs) of uniform widths similar to 4 nm but with three different average lengths, 200, 680, and 1100 nm. The viscosity average degrees of polymerization of the TOCNs were 250, 350, and 400, respectively. Self-standing TOCN and TOCN-coated poly(ethylene terephthalate) (PET) and poly(lactic acid) (PLA) films were prepared, and the optical, mechanical and gas-barrier properties of the films were evaluated in terms of nanofibril length. Only small differences in density, water content, and elastic modulus of the films were observed but TOCN films prepared from longer nanofibrils clearly showed higher tensile strengths, elongations at break and crystallinity indices. The oxygen barrier properties of the TOCN-coated PET and PLA films increased with increasing nanofibril length. In contrast, nanofibril length had almost no influence on water vapor-barrier properties. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据