3 dichloro-2- propyl) phosphate; tris (1; Organophosphate; photolytic degradation; kinetics; thermal degradation
Kinetics of thermal and photo-initiated release of Tris (1.3-dichloro-2-propyl) phosphate (TDCP) from the polyurethane foam (PUF) materials were studied using a validated chromatographic method with linear calibration curve in the range of 0.03-400 mu g mL(-1). Time dependence of TDCP leaching from foam samples was found to follow first-order kinetics; with rate constants directly dependent on ageing temperatures and intensity of UV radiation, rate constants for the thermally and photo initiated were 3.6 x 10(-3), 1.03 x 10(-2), 3.6 x 10(-2) and 3.94 x 10(-2) day(-1), respectively. Migration of TDCP from foam samples simulating skin or oral exposure were observed from all samples regardless of their ageing history, the presence of biological fluids found to enhance the migration rate. Oral exposure to foam material contains TDCP, which was simulated using the Head-over-Heels test, reveals that an average amount of similar to 1.7% wt./wt. of the total amount of TDCP was found to leach into biological fluids, and it significantly increased to similar to 6.0% wt./wt. due to ageing conditions. Direct contact between foam material and skin simulated by using the Contact Blotting test reveals that TDCP is transferred from both aged and un-aged samples at different rates, due to the presence of biological fluids; the transferred amount is increased with ageing conditions.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据