期刊
JOURNAL OF MATERIALS CHEMISTRY
卷 15, 期 10, 页码 1079-1083出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/b416007j
关键词
-
Templated mesoporous carbons containing graphitic structures and a well- developed porosity were synthesised by using mesoporous silica materials (i.e. SBA-15 and silica xerogel) as templates and polypyrrole as carbon precursor. The polypyrrole was synthesised by in situ polymerization of pyrrole which was infiltrated into the silica pores containing FeCl3. The carbonization of polypyrrole in presence of iron allows carbon structures with some degree of graphitic order to be formed. The samples were characterised by XRD, nitrogen sorption, TEM, Raman and elemental analysis. The results show that the templated carbons have BET surface areas > 1000 m(2) g(-1) and a porosity built up by two pore systems with sizes centred at similar to3-4 nm and at 10-14 nm. In addition, they have a good electrical conductivity due to the presence of graphitic structures in the carbon framework.