期刊
CARBON
卷 43, 期 3, 页码 559-566出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.carbon.2004.10.020
关键词
porous carbon, resins; activation; electrochemical properties, porosity
Mesoporous carbon was prepared from resol-type phenol-formaldehyde resin using mesoporous silica as template. By filling the resin into the pores of the template, followed by resin carbonization and template dissolution, mesoporous carbon preparation can be significantly simplified. Small-angle X-ray diffraction reflected the long-range ordering of the pores in the carbon. TEM and N-2-adsorption analysis showed that the carbon contained mesopores of different sizes and a high proportion of micropores. Electrochemical cyclic voltammetry was conducted in H2SO4 to examine the surface accessibility of the carbon for double layer formation. Microporous activated carbon, also from the resol resin, was prepared for comparison. Although the pore sizes are different, the double-layer capacitances per unit area for both carbons are similar at low potential sweep rates. However, the capacitance decline with the sweep rate was less significant for the mesoporous carbon. Upon gasification of the carbons to increase their surface area, the ultimate capacitance per unit carbon area was enhanced and the enhancement was slightly larger for the mesoporous carbon. It is suggested that the presence of mesopores has facilitated the electrolyte migration into carbon interior. A two-electrode capacitor assembled with the mesoporous carbon was shown to have a small resistance and still exhibited a capacitive behavior at high potential sweep rates. (C) 2004 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据