Macroporous monoliths of SiO2-Al2O3 cryogels were prepared. Macropores were generated by using ice crystals as the template, while the walls which surround the macropores were tailored as porous cryogels by freeze drying. Macropores and walls formed honeycomb-like structures, which were confirmed from scanning electron microscopy images of cross-sections of the samples. It was confirmed that the sizes of the macropores and the wall thicknesses were respectively in the ranges of 10-20 mu m and 200-500 nm. Al mapping analysis by energy dispersive X-ray diffractometry showed that Al atoms were homogeneously dispersed throughout the samples without local aggregation. Moreover, Raman spectroscopy and Al-27 NMR spectroscopy indicated that Al atoms were incorporated into the silica framework by forming an Al-O-Si polymeric network. Nitrogen adsorption-desorption measurements indicated that the walls were micro/mesoporous with high BET surface areas (>700 m(2) g(-1)) and large pore volumes (>0.45 cm(3) g(-1)). Moreover, NH3-TPD measurements revealed that the samples had acid sites, which allowed this material to be used as a solid acid catalyst.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据