JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 26, 期 16, 页码 3717-3723出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2005.12.002
关键词
precursors-organic; perovskites; electron microscopy; dielectric properties; SrBi2Nb2O9
The processing conditions, reaction mechanism, fine structure of the powders, microstructure, and dielectric properties of SrBiNb2O9 (SBN) were systematically studied. A relative density of > 80% was obtained using a two-step sintering process at moderate pressure. XRD showed that a single phase with the layered perovskite structure of SrBi2Nb2O9 (SBN) was formed after calcining at 600 degrees C. No intermediate phase was found during heat treatment at and above 600 degrees C. The crystallite size (D) and the effective strain (eta) were found to be 38.8 nm and 0.01475, respectively, while the particle size obtained from TEM was laid between 25 and 36 nm. SEM revealed that the average grain size after sintering at 900 degrees C for 4 h was 0.67 mu m. Dielectric constant and corresponding tangent loss were measured in the frequency range from 1 kHz to 1 MHz from which the Curie temperature (T-c) was found to be at 450 degrees C. (c) 2005 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据