期刊
JOURNAL OF ELECTRONIC MATERIALS
卷 45, 期 3, 页码 1328-1335出版社
SPRINGER
DOI: 10.1007/s11664-015-4027-7
关键词
Thick-film cooling device; brush printing; n-type Bi2Te2.7Se0.3; electrical property
资金
- National Basic Research Program of China (973-program) [2013CB632505]
- National Natural Science Foundation of China [11274248]
A simple, efficient and rapid brush-printing method has been developed for preparation of n-type Bi2Te2.7Se0.3 films approximately 100-150 mu m thick. Xray diffraction, scanning electron microscopy, electron probe microanalysis, and four-point probe measurements were used to characterize the crystal structure, composition, microstructure, and electrical properties of the films. The results showed that all the n-type Bi2Te2.7Se0.3 thick films were composed of single-phase Bi2Te2.7Se0.3; the grains in the films were randomly distributed in the low-temperature-annealed samples and predominantly oriented along the (00l) plane in samples annealed at temperatures > 673 K. sigma and the absolute value of alpha first increased substantially with increasing the annealing temperature in the range 573-673 K then decreased when the annealing temperature was increased further. The dependence of sigma and alpha on annealing temperature may be reasonably explained on the basis of the change in the microstructure induced by annealing. The performance of a prototype cooling device containing n-type Bi2Te2.7Se0.3 thick films was evaluated for temperature differences produced by use of different DC currents.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据