The effects of microwave irradiation on the crystallization of 40%CaO-40%SiO2-2O%A1(2)O(3) synthesized slag and actual blast furnace slag were investigated using a 28GHz multimode microwave irradiation system, a commercial microwave oven (2.45GHz), and an electric resistance furnace. While it was observed that the 2.45 GHz centimeter-wave had little effect on the samples, the 28 GHz millimeter-wave was found to accelerate crystallization significantly, especially at lower temperatures at which the crystalline phases are never generated by external heating. Further, the effects of the precipitated phases and impurities on the crystallization with the 28GHz microwave irradiation were investigated. The temperature of the glassy slag increased more rapidly when compared with the crystalline phases that exist in the actual blast furnace slag. In addition, a small amount of impurity was found to improve the heating property of the slags.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据