期刊
DENTAL MATERIALS
卷 23, 期 4, 页码 415-424出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.dental.2006.02.010
关键词
dentistry; dental casting investment material; dental refractory die material; phosphate-bonded investment; setting; burn-out; solid-state NMR spectroscopy; P-31 NMR spectroscopy
Objectives. To use P-31 solid-state MAS-NMR to determine the phosphorus compounds that occur in dental casting investment material: (a) as-received, (b) after setting and (c) after burn-out and discover whether such compounds are the same in each material across a product range. Methods. {H-1} High powered decoupling (HPDC) and {H-1} cross-polarization (CP) P-31 solid-state MAS-NMR spectroscopy at a resonance frequency of 121.4 MHz were used. Six commercial products were examined. Manufacturer's instructions were followed and a special liquid was used without dilution. Results. All products contain ammonium dihydrogen phosphate as the acid phosphate required for the setting reaction. All set by the formation of struvite and significant amounts of amorphous magnesium orthophosphate. In three products, lesser amounts of newberyite were present and in another the equivalent amorphous compound was formed. When burnt-out, magnesium metaphosphate or pyrophosphate was the dominant matrix compound. A higher burn-out temperature favoured pyrophosphate formation. Farringtonite was present to a lesser extent with the metaphosphate. Significance. Compounds that were not detected in earlier X-ray powder diffraction spectroscopy studies were detected by NMR, notably amorphous and glassy compounds (magnesium orthophosphate in set investment and magnesium metaphosphate in burnt-out material). The variation between products was significant and far greater than expected from the published scientific literature. Since the formation of compounds is affected by technical procedure and ambient conditions, these findings could offer some insight into the cause of the unpredictability of expansion measurements between laboratories. Further research is being undertaken.(C) 2006 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据