SOLAR ENERGY
卷 81, 期 10, 页码 1280-1284出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.solener.2006.12.005
关键词
surface states; conductivity measurements; Pt/TiO2 thin film; effect of atmospheres
In this paper, the surface states of Pt/TiO2 thin film were tested in air, H, and N-2 flows. Pt/TiO2 was prepared by means of photoreduction of PtCl62- on anatase nano-TiO2 powders and was coated on the microscopy glass using powder sol technique. Powder con ductivitv method was applied in the analysis of surface states. The experimental results show that a new surface state was formed in air flow; which was 0.43 eV lower than the conduction band edge of TiO2. In N-2 flow, three surface states, with the energy levels of 0.42, 0.62 and 0.90 eV, respectively, were detected. Compared with that tested in airflow, 0.42 and 0.62 eV could be attributed to Pt and floating bond of TiO2 respectively, while 0.90 eV might have resulted from the Ti3+ formed at high temperature in N-2 flow. The conductivity of the sample tested in H, flow increased significantly and was almost unchanged with temperature, which could be interpreted by the dissociative adsorption of H, on Pt. (c) 2007 Elsevier Ltd. All riahts reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据