JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 313, 期 2, 页码 293-299出版社
ELSEVIER
DOI: 10.1016/j.jmmm.2007.01.010
关键词
co-precipitation; fine particles; nanoferrites; spinel
Co1-xZnxFe2O4 nanoparticles were prepared by co-precipitation method with x varying from 0 to 1.0. The powder samples were characterized by X-ray diffraction (XRD), vibrating sample magnetometer (VSM) and Fourier transform infrared spectroscopy (FTIR). The average crystallite sizes of the particles were determined from XRD. X-ray analysis showed that the samples were cubic spinel. The average crystallite size (D-aveXR) of the particles precipitated was found to vary from 6.92 to 12.02 nm decreasing with the increase in zinc substitution. The lattice constant (a(o)) increased with the increase in zinc substitution. The specific saturation magnetization (M-S) of the particles was measured at room temperature. The magnetic parameters such as M-S, H-c, and M-r were found to decrease with the increase in zinc substitution. FTIR spectra of the Co1-xZnxFe2O4 with x varying from 0 to 1.0 in the range 400-4000cm(-1) were reported. The spinel structure and the crystalline water adsorption of Co1-xZnxFe2O4 nanoparticles were studied by using FTIR. (c) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据