JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 308, 期 2, 页码 305-312出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmmm.2006.06.005
关键词
hysteresis; magnetic iron oxides; magnetic losses; nanoparticles; specific heating power
Magnetic iron oxide nanoparticle powders were investigated in order to optimise the specific hysteresis losses for biomedical heating applications. Different samples with a mean particle size in the transition range from superparamagnetic to ferromagnetic behaviour (i.e. 10-100 nm) were prepared by two different chemical precipitation routes. Additionally, the influence of milling and annealing on hysteresis losses of the nanoparticles was investigated. Structural investigations of the samples were carried out by X-ray diffraction, measurement of specific surface area, and scanning and transmission electron microscopy. The dependence of hysteresis losses of minor loops on the field amplitude was determined using vibrating sample magnetometry and caloric measurements. For small field amplitudes, a power law was found which changes into saturation at amplitudes well above the coercive field. Maximum hysteresis losses of 6.6 J/kg per cycle were observed for milled powder. For field amplitudes below about 10 kA/m, which are especially interesting for medical and technical applications, hysteresis losses of all investigated powders were at least by one order of magnitude lower than reported for magnetosomes of comparable size. (c) 2006 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据