TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
卷 17, 期 1, 页码 195-199出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/S1003-6326(07)60071-5
关键词
vanadium redox battery; graphite felt; electrochemical oxidation
The graphite felt was oxidized at a positive electrode potential in sulfuric acid solution. The electrochemical performance of the treated graphite felt served as electrode for vanadium redox battery was investigated with FT-IR, SEM, XPS, BET, cyclic voltammetry and testing VRB system, respectively. The results show that the molar ratio of 0 to C increases from 0.085 to 0.15 due to the increase of - COOH functional groups during electrochemical oxidation treatment, and the GF surface is eroded by electrochemical oxidation, resulting in the surface area increase from 0.33 m(2)/g to 0.49 m(2)/g. The VRB with modified GF electrode exhibits excellent performance under a current density of 30 mA/cm(2). The average current efficiency reaches 94% and average voltage efficiency reaches 85%. The improvement of electrochemical activity for the electrode is ascribed to the increase of the number of - COOH group and the special surface of GF.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据