The graded material of Ti6Al4V-Rene88DT superalloy, which has shown the potential to be applied in aeroengines, was fabricated from prealloyed metal powders using the technique of laser rapid forming (LRF). A compositional gradient, from 100 pet Ti6Al4V to T16Al4V-38 pet Rene88DT, was achieved within a thickness of laser deposit of 54 mm. The solidification behavior and the phase evolution of the compositionally graded material were studied. The results of the X-ray diffraction (XRD) analysis together with the metallographic study showed that a series of phase evolutions, alpha + beta -> alpha + beta + Ti2Ni -> beta + Ti2Ni, along the compositional gradient have occurred. The hardness value of the graded material was measured along the compositional gradient, and the results were explained in terms of the various phases present. The condition for columnar-to-equiaxed transition observed in the graded material was explained, based on Hunt's criterion. Finally, the morphology of beta + Ti2Ni anomalous eutectic is discussed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据