Forensic Discrimination of Aluminum Foil by SR-XRF and ICP-AES

The application of synchrotron radiation X-ray fluorescence spectrometry (SR-XRF) was investigated for the forensic discrimination of aluminum foil by comparisons of the elemental components. Small fragments (1 X 1 mm) were taken from 4 kinds of aluminum foils produced by different manufactures and used for measurements of the XRF spectrum at BL37XU of SPring-8. A comparison of the XRF spectra was effective for the discrimination of aluminum foils from different sources, because significant differences were observed in the X-ray peak intensities of Fe, Cu, Zn, Ga, Zr and Sn. These elements, except for Zr and Sri in the aluminum foils and NIST SRM1258 (Aluminium Alloy 6011), were also determined by inductively coupled plasma atomic emission spectrometry (ICP-AES). The observed values of Fe, Cu, Zn and Ga in NIST standard samples by ICP-AES showed satisfactorily good agreements with the certified or information values with relative standard deviations from 1.1% for Zn to 6.7% for Ga. The observed values for the aluminum foils by ICP-AES were compared with those by SR-XRF. Correlation coefficients from 0.997 for Cu/Fe to 0.999 for Zn/Fe and Ga/Fe were obtained between the ratio of the elemental concentration by ICP-AES and normalized the X-ray intensity by SR-XRF. This result demonstrates that a comparison of the normalized X-ray intensity is nearly as effective for the discrimination of aluminum foils as quantitative analysis by ICP-AES. Comparisons of the analytical results by SR-XRF allow the discrimination of all aluminum foils using only a 1 mm(2) fragment with no destruction of the samples.