期刊
BULLETIN OF MATERIALS SCIENCE
卷 31, 期 5, 页码 713-717出版社
INDIAN ACAD SCIENCES
DOI: 10.1007/s12034-008-0112-3
关键词
Fe3O4 nanoparticles; particle size; crystallinity; magnetic property; Schikorr reaction
Magnetite nanoparticles were prepared by hydrothermal synthesis under various initial ferrous/ferric molar ratios without adding any oxidizing and reducing agents in order to clarify effects of the molar ratio on the reaction mechanism for the formation of magnetite nanoparticles. The magnetite nanoparticles prepared were characterized by a scanning electron microscope, powder X-ray diffractometer, and superconducting quantum interference device (SQUID). At the molar ratio corresponding to the stoichiometric ratio in the synthesis reaction of magnetite from ferrous hydroxide and goethite, the nucleation of magnetite crystals progressed rapidly in an initial stage of the hydrothermal synthesis, resulting in formation of the magnetite nanoparticles having a smaller size and a lower crystallinity. On the other hand, at higher molar ratios, the particle size and crystallinity increased with increasing molar ratio because using surplus ferrous hydroxide the crystallites of magnetite nanoparticles grew up slowly under hydrothermal conditions according to the Schikorr reaction. The magnetite nanoparticles prepared under various molar ratios had good magnetic properties regardless of the molar ratio.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据