TRIBOLOGY-MATERIALS SURFACES & INTERFACES
卷 7, 期 3, 页码 114-121出版社
TAYLOR & FRANCIS LTD
DOI: 10.1179/1751584X13Y.0000000039
关键词
Alumina; Carbon steel; Corrosion; Erosion; Erosion-Corrosion; Microfluid; Nanofluid; Sea water
资金
- research council of Razi University
This work presents the results of an experimental study on surface damage due to erosion, corrosion and their interactive effect in sea water in the presence or absence of 1 g L-1 suspended nanosize as well as microsize Al2O3 particles. Erosion and erosion-corrosion tests have been conducted on low carbon steel targets using a rotating cylinder system. It is found that nano-and microsize particles act as inhibitors and decrease the pure corrosion rate in comparison to base fluids free of these particles, but over time, the inhibitory effect of microparticles is lost. The presence of microparticles causes more severe steel erosion than sea water, whereas the difference between nanofluid and sea water is not significant. In spite of the effects of nanoparticles on pure corrosion and net erosion, mass loss due to erosion-corrosion in a nanofluid is much higher that the base fluid but is less than the fluid containing microsize particles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据