期刊
ACTA METALLURGICA SLOVACA
卷 20, 期 2, 页码 200-208出版社
TECHNICKA UNIV V KOSICIACH & HUTNICKA FAKULTA
DOI: 10.12776/ams.v20i2.290
关键词
Calcium phosphate; Magnesium alloy; Electrochemical impedance spectroscopy; Light microscopy; Electrodeposition
资金
- European regional development fund and Slovak state budget by the project Research centre of the University of Zilina [ITMS 26220220183]
- Unique equipment for evaluation of tribological properties of machines parts surfaces [ITMS 26220220048]
- VEGA [1/0831/13]
Electrodeposition process of calcium phosphate (CaP) was performed at various temperatures on AZ31 magnesium alloy and the influence on corrosion resistance of the alloy covered by CaP was investigated by electrochemical tests supported by photodocumentation. The electrodeposition treatment was performed by potential controlled method in water solution of Ca(NO3)(2).4H(2)O, NH4H2PO4 and H2O2. The difference in the process of CaP formation at various temperatures was described using diagrams of current density time dependence. Corrosion measurements were performed in 0.9% NaCl solution at 22 +/- 2 degrees C using electrochemical impedance spectroscopy. According to corrosion resistance results, the optimal temperature for CaP electrodeposition process was chosen.