RSC ADVANCES
卷 6, 期 27, 页码 22764-22776出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c5ra27451f
关键词
-
资金
- European Union's Seventh Framework Programme (FP7) [264115-STREAM]
Advanced flame retardant epoxy resins, environmentally friendly, with different contents of a new oligophosphonate (PFR), were prepared using dicyandiamide as a hardener and 1,1-dimethyl-3-phenylurea as an accelerator. PFR, with a high phosphorus content, was synthesized by polycondensation reaction of phenylphosphonic dichloride with a phosphorus-containing bisphenol, namely bis((6-oxido-6H-dibenz[c,e][1,2]oxaphosphorinyl)-(4-hydroxyaniline)methylene)-1,4-phenylene. The bisphenol was prepared by reacting 9,10-dihydro-oxa-10-phosphaphenanthrene-10-oxide with an imine bisphenol resulting from the condensation of 4-aminophenol with terephthalaldehyde. The structure and morphology of cured epoxy resins were evaluated by Fourier transform infrared spectroscopy and scanning electron microscopy (SEM) analysis, respectively. Differential scanning calorimetry analysis revealed that cured epoxy resins containing PFR possessed slightly higher glass transition temperatures than phosphorus-free cured epoxy resin. Thermogravimetric analysis and limiting oxygen index values indicated that the incorporation of PFR into epoxy resin substantially enhanced the thermal stability and flame retardancy of the char layer at high temperature. The surface morphology of the char residue was studied by SEM measurements. The kinetic processing of thermogravimetric data was carried out using Friedman and Vyazovkin methods. The lifetime prediction analysis established that the fire-resistant phosphorus-containing epoxy resins could be used at a constant temperature of 200 degrees C up to 620-630 minutes. The new PFR can be successfully used as a very efficient flame retardant for improving the fire-resistance properties of epoxy resins.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据