期刊
CELLULOSE
卷 25, 期 2, 页码 1031-1046出版社
SPRINGER
DOI: 10.1007/s10570-017-1624-z
关键词
Cellulose nanocrystals; Catalytic solvolysis of cellulose; Phosphotungstic acid; Shape and size; Crystallinity; Thermostability
资金
- Russian Science Foundation [16-13-10148]
The novel system [acetic acid/phosphotungstic acid (H3PW12O40)/octanol] was proposed for catalytic solvolysis of cellulose and for obtaining cellulose nanocrystals (CNC). Several alternative experiments involving mixtures with different compositions were carried out; reaction time was also varied. CNC particles from cotton, linen, softwood and hardwood cellulose were prepared in the experiments performed for 40 min in the presence of 0.25 mol% of the heteropolyacid. CNC samples were characterized by transmission electron microscopy and atomic force microscopy, X-ray diffraction analysis, and thermogravimetric analysis. It was established that the resulting nanoparticles had high crystallinity and rod-like shape; their length varied from 160 to 400 nm (cotton CNC had the shortest length, and linen CNC had the longest length), and CNC thickness ranged from 6 to 10 nm. Thermal stability of CNC was lower than that of initial celluloses and decreasing in the following sequence: cotton > softwood > hardwood > linen cellulose.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据