期刊
RSC ADVANCES
卷 8, 期 67, 页码 38631-38640出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c8ra05890c
关键词
-
资金
- National Natural Science Foundation of China [11504267, 11504269]
- Doctoral Fund of Tianjin Normal University [52XB1518]
- Tianjin municipal education commission scientific research project [2017KJ238]
Reduced graphene oxide coated carbon cloth has been used as a substrate for the growth of ultrafine MnO2 nanowires (CC/RGO/MnO2), forming binder-free and flexible supercapacitor electrode materials. The experimental results indicate that a maximum area-specific capacitance of 506.8 mF cm(-2) was gained from the CC/RGO/MnO2 electrode at the current density of 0.128 mA cm(-2). Furthermore, the electrode exhibits excellent cycling stability (98.6% specific capacitance was still retained after 10000 galvanostatic charge-discharge (GCD) tests when the current density was 1.28 mA cm(-2)). What's more, the area-specific capacitance of the CC/RGO/MnO2 electrode was hardly changed, when the electrode was operated under bending mechanical conditions. In addition, the charge storage performance and mechanism of the MnO2 nanostructures was discussed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据