MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
卷 276, 期 1-2, 页码 283-287出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/S0921-5093(99)00492-X
关键词
low cycle fatigue; elevated temperature; cyclic stress response; fatigue life; fracture morphology
The low cycle fatigue properties of an aluminium alloy (Al-12Si-CuMgNi), obtained at a temperature of 623 K, are reported and discussed. The properties studied include cyclic stress response, fatigue life and nature of fracture as a function of applied strain amplitude. The alloy exhibits moderate cyclic softening from the very first cycle till failure at all the strain amplitudes tested. The variation of high strain, low cycle fatigue life (measured in terms of number of reversals to failure, 2N(f)) with plastic strain amplitude (Delta epsilon(p)/2) is seen to follow a single-slope Coffin-Manson power-law relationship. The alloy is seen to fail during fatigue loading by a mixture of quasi-cleavage fracture and microdimples of high spatial density. Finally, a comparison of the fatigue life of the aluminium alloy in the over-aged (OA) condition (obtained from the present study) with that of the alloy in a highly over-aged (HOA) condition of an earlier study reveals that the effect of ageing on the low cycle fatigue resistance depends on the damage parameter considered, viz. Delta epsilon(p)/2 or Delta W-p, the average plastic strain energy per cycle. (C) 2000 Elsevier Science S.A. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据