期刊
BIOMATERIALS
卷 31, 期 25, 页码 6582-6588出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.biomaterials.2010.05.018
关键词
Zwitterionic; Iron oxide nanoparticles; Biomimetic linkage; Ultra-low fouling; MRI (magnetic resonance imaging); Targeting
资金
- Office of Naval Research [N000140910137]
- National Science Foundation [DMR-0705907]
Multifunctional magnetic nanoparticles (MNPs) modified by a zwitterionic polymer (pCBMA-DOPA(2)) containing one poly(carboxybetaine methacrylate) (pCBMA) chain and two 3,4-dihydroxyphenyl-L-alanine (DOPA) residue groups were developed. Results showed that MNPs modified by pCBMA were not only stable in complex media, but also provided abundant functional groups for ligand immobilization. The pCBMA-DOPA(2) MNPs had a hydrodynamic particle size of about 130 nm, a strong saturation magnetization of 110.2 emu/g Fe and a high transverse relaxivity of 428 mM(-1) s(-1). Long-term stability in phosphate-buffered saline (PBS) and 10% NaCl solution was achieved for over six months. Compared to MNPs coated with dextran, pCBMA-DOPA(2) MNPs presented better stability in 100% human blood serum at 37 C. Macrophage cell uptake studies revealed that the uptake ratio of pCBMA-DOPA(2) MNPs was much lower than that of dextran MNPs. Furthermore, quantitative analysis results showed that after pCBMA-DOPA(2) MNPs were conjugated with a targeting RGD peptide, uptake by human umbilical vein endothelial cell (HUVEC) was notably increased, which was further visualized by magnetic resonance imaging (MRI). (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据