BIOMACROMOLECULES
卷 12, 期 4, 页码 961-969出版社
AMER CHEMICAL SOC
DOI: 10.1021/bm101330w
关键词
-
资金
- Swedish Foundation for Strategic Research, Biomime
- Swedish Centre for Biomimetic Fiber Engineering
- Wallenberg Wood Science Centre
- Designcell project
- Lyckeby Research Foundation
The Young's modulus of multilayer films containing nanofibrillated cellulose (NFC) and polyethyleneimine (PEI) was determined Using the strain-induced elastic buckling instability for mechanical measurements (SLEBIMM) technique.(1) Multilayer films were built up on polydimethylsiloxane substrates using electrostatic layer-by-layer assembly. At 50% relative humidity, SIEBIMM gave a constant Young's modulus of 1.5 +/- 0.2 GPa for 35-75 run thick films. Conversely, in vacuum, the Young's modulus was 10 times larger, at 17.2 +/- 1.2 GPa. A slight decrease in buckling wavelength with increasing strain was observed by scanning electron microscopy with in situ compression, and above 10% strain, extensive cracking parallel to the compressive direction occurred. We conclude that whereas PEI acts as a glue to hold multiple layers of NFC together, it prevents full development of hydrogen bonding and specific fibril-fibril interactions, and at high humidity, its hygroscopic nature decreases the elastic modulus when compared with pure NFC films.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据