JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A
卷 18, 期 4, 页码 1987-1992出版社
A V S AMER INST PHYSICS
DOI: 10.1116/1.582459
关键词
-
In this study, we introduce a new diamondlike carbon (DLC) film providing a friction coefficient of 0.001 and wear rates of 10(-9)-10(-10) mm(3)/N m in inert-gas environments (e.g., dry nitrogen and argon). The him was grown on steel and sapphire substrates in a plasma enhanced chemical vapor deposition system that uses a hydrogen-rich plasma. Employing a combination of surface and structure analytical techniques, we explored the structural chemistry of the resultant DLC films and correlated these findings with the friction and wear mechanisms of the films. The results of tribological tests under a 10 N load (creating initial peak Hertz pressures of 1 and 2.2 GPa on steel and sapphire test pairs, respectively) and at 0.2 to 0.5 m/s sliding velocities indicated that a close correlation exists between the friction and wear coefficients of DLC films and the source gas chemistry. Specifically, films grown in source gases with higher hydrogen-to-carbon ratios had the lowest friction coefficients and the highest wear resistance. The lowest friction coefficient (0.001) was achieved with a film on sapphire substrates produced in a gas discharge plasma consisting of 25% methane and 75% hydrogen. (C) 2000 American Vacuum Society. [S0734-2101(00)14204-6].
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据